fast stirrup
Hi, just try to tune HT-PLA from Spectrum The Filament. Filament has been dryer for 12hours. I run already the calibrations for pressure. Advanced and flowrate. When I look at the Punk cube corners it looks like every second layer I see this small difference. Any ideas what that could be?
meager owl
I am facing the same issue. ASA in this case, but happens with all filaments. Usually using Prusa Slicer, to rule out any Slicer related issues I have set up a fresh Orca Slicer and used a generic profile
meager owl
@fast stirrup What is your current acceleraton for the outisde parameter? I have just set it down from 15000 to 2000 and the ripple is almost gone. can you try what happens on your side with this?
closer look: It has onlyx visibly reduced, still there
spiral agate
As I'm running a IDEX 500 my Accl Settings are already very low.
I did Run PA Lines severeal times and adjusted acordingly.
What I just noticed is the Flow Change every 2nd Layer for the Inner Wall? Why is Orcaslicer donig this. Which Seeting is causing this?
spiral agate
Where can i find this Testprint?
spiral agate
Breh, do you even calibrate PA?
That’s all this is.
Corners turn to licorice rop...
Yes I would aggree, but i confuses me that this was visible every 2nd Layer, but now with this strange Flow change I need to Test again.
THX all, for your input,will reply
meager owl
Where can i find this Testprint?
just create a cube 50x50x50 on the buildplate. 2 walls, few or no infill. then, use the PA Tuning macro: https://os.ratrig.com/docs/configuration/calibration/#initialize_pa_tuning
See also https://ellis3dp.com/Print-Tuning-Guide/articles/index_pressure_advance.html